Large-sized La2O3-TiO2-SiO2 Amorphous Oxide Fabricated by Hot Press Sintering
Li Ren-Yi1,2; Li Xiao-Yu2; Li Jian-Qiang2; Zhao Jian-Ling1; Ma Xiao-Guang2; He Gang3; Li Jiang-Tao3
2017-08-01
发表期刊JOURNAL OF INORGANIC MATERIALS
ISSN1000-324X
卷号32期号:8页码:851-856
摘要La2O3-TiO2 amorphous oxide has prospective applications because of its remarkable optical properties. However, due to its poor glass-forming abilities, it is difficult to prepare this material in a traditional way. The containerless solidification method can overcome this shortcoming, but the formed material size is generally restricted to be less than 10 mm. In order to obtain large-sized La2O3-TiO2 amorphous oxide, a small amount of SiO2 was added to the La2O3-TiO2 oxide system to form the amorphous oxide powders by aerodynamic levitation furnace. Subsequently, the high-density La2O3-TiO2-SiO2 materials were fabricated by vacuum hot press sintering. Compositions and microstructure properties were systematically studied by XRD and SEM. The results showed that SiO2 could improve the glass-forming ability of La2O3-TiO2. The raw powders made by aerodynamic levitation furnace were completely non-crystal, while the sintered samples had weak crystallization, which affected fully densification of sintered samples. There was a small amount of porosity in the high-density product made by vacuum hot press sintering. In addition, sintering densification mechanism of the La2O3-TiO2-SiO2 amorphous powders was analyzed. Finally, the optical property of hot pressed La2O3-TiO2-SiO2 material was investigated. It is found that La2O3-TiO2-SiO2 material still kepts high refractive index of above 2.2 in the visible light region. Small amount addition of SiO2 species improves the glass-forming abilities, yet decreases the refractive index slightly.
关键词Amorphous Oxide Aerodynamic Levitation Hot-press Sintering Large-size Densification
文章类型Article
WOS标题词Science & Technology ; Technology
DOI10.15541/jim20160619
收录类别SCI
语种英语
关键词[WOS]OPTICAL-PROPERTIES ; GLASS ; NANOCERAMICS ; TRANSPARENT ; ALUMINA
WOS研究方向Materials Science
WOS类目Materials Science, Ceramics
WOS记录号WOS:000405927500011
引用统计
文献类型期刊论文
条目标识符http://ir.ipe.ac.cn/handle/122111/22984
专题湿法冶金清洁生产技术国家工程实验室
作者单位1.Hebei Univ Technol, Sch Mat Sci & Engn, Tianjin 300130, Peoples R China
2.Chinese Acad Sci, Key Lab Green Proc & Engn, Inst Proc Engn, Natl Engn Lab Hydrometallurg Cleaner Prod Technol, Beijing 100190, Peoples R China
3.Chinese Acad Sci, Tech Inst Phys & Chem, Beijing 100190, Peoples R China
推荐引用方式
GB/T 7714
Li Ren-Yi,Li Xiao-Yu,Li Jian-Qiang,et al. Large-sized La2O3-TiO2-SiO2 Amorphous Oxide Fabricated by Hot Press Sintering[J]. JOURNAL OF INORGANIC MATERIALS,2017,32(8):851-856.
APA Li Ren-Yi.,Li Xiao-Yu.,Li Jian-Qiang.,Zhao Jian-Ling.,Ma Xiao-Guang.,...&Li Jiang-Tao.(2017).Large-sized La2O3-TiO2-SiO2 Amorphous Oxide Fabricated by Hot Press Sintering.JOURNAL OF INORGANIC MATERIALS,32(8),851-856.
MLA Li Ren-Yi,et al."Large-sized La2O3-TiO2-SiO2 Amorphous Oxide Fabricated by Hot Press Sintering".JOURNAL OF INORGANIC MATERIALS 32.8(2017):851-856.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Li Ren-Yi]的文章
[Li Xiao-Yu]的文章
[Li Jian-Qiang]的文章
百度学术
百度学术中相似的文章
[Li Ren-Yi]的文章
[Li Xiao-Yu]的文章
[Li Jian-Qiang]的文章
必应学术
必应学术中相似的文章
[Li Ren-Yi]的文章
[Li Xiao-Yu]的文章
[Li Jian-Qiang]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。