Removal of Phosphorus in Silicon by the Formation of CaAl2Si2 Phase at the Solidification Interface
Sun, Liyuan; Wang, Zhi; Chen, Hang; Wang, Dong; Qian, Guoyu
2017
发表期刊METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE
ISSN1073-5615
卷号48期号:00页码:420
摘要

To fully understand the role of CaAl2Si2 phase in concentrating the non-metallic impurity phosphorus, an experiment of directional solidification of Al-70 at. pct Si alloy with extreme small lowering rate 0.05 mm min(-1) was carried out. With good dynamic condition for the diffusion of impurity (Ca, Al, P) from silicon to the S/L interface, the CaAl2Si2 phase with 0.6-0.7 at. pct P was successfully observed by Electron Probe Micro Analyzer (EPMA), and its distribution character was originally presented. This impurity phase was widely detected in the refined sample but only at the interface of silicon crystal and Al-Si alloy which contributed to the deep removal of impurity P. The formation mechanism of CaAl2Si2-P phase was thus explored, in which the microsegregation and concentration of element P, Ca, Al in front of S/L interface were crucial. After acid leaching, the P content decreased from the original 23 ppm to below 5 ppm. Compared with normal solidification, a 16 pct higher removal efficiency of P was obtained in this study. (C) The Minerals, Metals & Materials Society and ASM International 2016

关键词Metallurgical-grade Silicon Si-al Melt Sn-si Calcium Purification Enrichment Titanium System Boron
文章类型Article
DOI10.1007/s11663-016-0848-x
WOS记录号WOS:000392295500042
引用统计
文献类型期刊论文
条目标识符http://ir.ipe.ac.cn/handle/122111/23532
专题研究所(批量导入)
通讯作者Wang, Zhi
推荐引用方式
GB/T 7714
Sun, Liyuan,Wang, Zhi,Chen, Hang,et al. Removal of Phosphorus in Silicon by the Formation of CaAl2Si2 Phase at the Solidification Interface[J]. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE,2017,48(00):420.
APA Sun, Liyuan,Wang, Zhi,Chen, Hang,Wang, Dong,&Qian, Guoyu.(2017).Removal of Phosphorus in Silicon by the Formation of CaAl2Si2 Phase at the Solidification Interface.METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE,48(00),420.
MLA Sun, Liyuan,et al."Removal of Phosphorus in Silicon by the Formation of CaAl2Si2 Phase at the Solidification Interface".METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE 48.00(2017):420.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Sun, Liyuan]的文章
[Wang, Zhi]的文章
[Chen, Hang]的文章
百度学术
百度学术中相似的文章
[Sun, Liyuan]的文章
[Wang, Zhi]的文章
[Chen, Hang]的文章
必应学术
必应学术中相似的文章
[Sun, Liyuan]的文章
[Wang, Zhi]的文章
[Chen, Hang]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。