CAS OpenIR
phosphateenrichmentmechanismincaosio2feofe2o3p2o5steelmakingslagswithlowerbinarybasicity
Li Jinyan1; Zhang Mei1; Guo Min1; Yang Xuemin2
2016
Source Publicationinternationaljournalofmineralsmetallurgyandmaterials
ISSN1674-4799
Volume23Issue:5Pages:520
AbstractThe addition of silica to steelmaking slags to decrease the binary basicity can promote phosphate enrichment in quenched slag samples. In this study, we experimentally investigated phosphate enrichment behavior in CaO-SiO_2-FeO-Fe_2O_3-P_2O_5 slags with a P_2O_5 content of 5.00% and the binary basicity B ranging from 1.0 to 2.0, where the (%Fe_tO)/(%CaO) mass percentage ratio was maintained at 0.955. The experimental results are explained by the defined enrichment degree R_(C_2S-C_3P) of solid solution 2CaO·SiO_2-3CaO·P_2O_5 (C_2S-C_3P), where R_(C_2S-C_3P) is a component of the developed ion and molecule coexistence theory (IMCT)-N_i model for calculating the mass action concentrations N_i of structural units in the slags on the basis of the IMCT. The asymmetrically inverse V-shaped relation between phosphate enrichment and binary basicity B was observed to be correlated in the slags under applied two-stage cooling conditions. The maximum content of P_2O_5 in the C_2S-C_3P solid solution reached approximately 30.0% when the binary basicity B was controlled at 1.3.
Language英语
Document Type期刊论文
Identifierhttp://ir.ipe.ac.cn/handle/122111/32377
Collection中国科学院过程工程研究所
Affiliation1.北京科技大学
2.中国科学院过程工程研究所
Recommended Citation
GB/T 7714
Li Jinyan,Zhang Mei,Guo Min,et al. phosphateenrichmentmechanismincaosio2feofe2o3p2o5steelmakingslagswithlowerbinarybasicity[J]. internationaljournalofmineralsmetallurgyandmaterials,2016,23(5):520.
APA Li Jinyan,Zhang Mei,Guo Min,&Yang Xuemin.(2016).phosphateenrichmentmechanismincaosio2feofe2o3p2o5steelmakingslagswithlowerbinarybasicity.internationaljournalofmineralsmetallurgyandmaterials,23(5),520.
MLA Li Jinyan,et al."phosphateenrichmentmechanismincaosio2feofe2o3p2o5steelmakingslagswithlowerbinarybasicity".internationaljournalofmineralsmetallurgyandmaterials 23.5(2016):520.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li Jinyan]'s Articles
[Zhang Mei]'s Articles
[Guo Min]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li Jinyan]'s Articles
[Zhang Mei]'s Articles
[Guo Min]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li Jinyan]'s Articles
[Zhang Mei]'s Articles
[Guo Min]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.