前驱体热解氮化硼碳化硅复相泡沫陶瓷的抗氧化与高温隔热性能研究
沈志洵; 戈敏; 陈明伟; 钱扬保; 张伟刚
2012
Source Publication无机材料学报
ISSN1000-324X
Volume27Issue:12Pages:1306
AbstractA kind of BN/SiC open-cell ceramic foams were fabricated from complex co-polymeric precursors of polycarbosilane and tris(methylamino)borane B(NHCH3)(3) using a high-pressure pyrolysis foaming technique. The obtained foams exhibited cell sizes ranging from 1 mm to 5 mm with bulk densities varying from 0.44 g/cm(3) to 0.73 g/cm(3), depending on the proportion of the starting precursors. Studies on the microstructure and thermal property of the porous ceramics showed that the addition of BN into SiC could improve dramatically the oxidation resistance from 800 to 1100 degrees C. The compression strength of the composite foams was 5-10 times higher than that of pure SiC foam, which increased with increasing of BN content in the ceramic foams. Heat insulation performance of the ceramic foam fabricated from the starting precursors with a proportion of 1:1 in weight was analyzed by a device designed for insulation performance at high-temperature. When the temperature at the center point of hot surface of the foam was 1400 degrees C, the temperature at the center point of the back achieved only 280 degrees C. The heating history of the foam was simulated by finite- difference method, and the results showed that thermal conductivity of the composite foam was 4.0 W/(m.K), which was almost identical to the experimental result.
Language英语
Document Type期刊论文
Identifierhttp://ir.ipe.ac.cn/handle/122111/37368
Collection中国科学院过程工程研究所
Affiliation中国科学院过程工程研究所
First Author Affilication中国科学院过程工程研究所
Recommended Citation
GB/T 7714
沈志洵,戈敏,陈明伟,等. 前驱体热解氮化硼碳化硅复相泡沫陶瓷的抗氧化与高温隔热性能研究[J]. 无机材料学报,2012,27(12):1306.
APA 沈志洵,戈敏,陈明伟,钱扬保,&张伟刚.(2012).前驱体热解氮化硼碳化硅复相泡沫陶瓷的抗氧化与高温隔热性能研究.无机材料学报,27(12),1306.
MLA 沈志洵,et al."前驱体热解氮化硼碳化硅复相泡沫陶瓷的抗氧化与高温隔热性能研究".无机材料学报 27.12(2012):1306.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[沈志洵]'s Articles
[戈敏]'s Articles
[陈明伟]'s Articles
Baidu academic
Similar articles in Baidu academic
[沈志洵]'s Articles
[戈敏]'s Articles
[陈明伟]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[沈志洵]'s Articles
[戈敏]'s Articles
[陈明伟]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.