Study on salt spray corrosion of Ni-graphite abradable coating with 80Ni20Al and 96NiCr-4Al as bonding layers
Xu, Cunguan1,2; Du, Lingzhong1; Yang, Bin2; Zhang, Weigang1; Zhang, WG
2011-05-25
Source PublicationSURFACE & COATINGS TECHNOLOGY
ISSN0257-8972
Volume205Issue:17-18Pages:4154-4161
AbstractTwo kinds of Ni-graphite abradable coating systems (coating system A with 80Ni20Al bond coating and coating system B with 96NiCr-4Al bond coating) were prepared. The top and the bond coatings were independently deposited by different techniques of flame and plasma spraying. Corrosion behavior of the coating systems was investigated via the electrochemical and salt spray corrosion tests. Open-circuit potential and polarization tests were carried out in an oxygen-saturated 5 wt.% NaCl neutral solutions at 35 degrees C. It was found that the 80Ni20Al coating exhibited the lowest corrosion resistance. Results of the salt spray corrosion (SSC) tests support a corrosion mechanism in the Ni-graphite coating being a crevice corrosion, which leads to loose corrosion products accumulated on the surface of the coating systems. For coating system A, analysis of the corrosion damage of the bonding layer showed a prevalent localized attack on intersplat boundaries. For coating system B, the bonding layer exhibited less corrosion, but the matrix of the top coating close to the interface corroded heavily due to a galvanic coupling between these two different coating layers. Experimental results after 960 h SSC tests showed that the bonding strength decreased to 3.5 MPa and 2.6 MPa for coating systems A and B, respectively. (C) 2011 Elsevier B.V. All rights reserved.
KeywordAbradable Coating Bond Coating Thermal Spraying Salt Spray Corrosion Polarization
SubtypeArticle
WOS HeadingsScience & Technology ; Technology ; Physical Sciences
DOI10.1016/j.surfcoat.2011.03.007
Indexed BySCI
Language英语
WOS KeywordSTAINLESS-STEEL ; ELECTROCHEMICAL-BEHAVIOR ; MECHANICAL-PROPERTIES ; WEAR BEHAVIOR ; PERFORMANCE ; EVOLUTION ; OXIDATION ; ALLOY ; AL
WOS Research AreaMaterials Science ; Physics
WOS SubjectMaterials Science, Coatings & Films ; Physics, Applied
WOS IDWOS:000291295200005
Citation statistics
Cited Times:22[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Version出版稿
Identifierhttp://ir.ipe.ac.cn/handle/122111/4871
Collection多相复杂系统国家重点实验室
Corresponding AuthorZhang, WG
Affiliation1.Chinese Acad Sci, Inst Proc Engn, State Key Lab Multiphase Complex Syst, Beijing 100190, Peoples R China
2.Univ Sci & Technol Beijing, State Key Lab Adv Met & Mat, Beijing 100083, Peoples R China
Recommended Citation
GB/T 7714
Xu, Cunguan,Du, Lingzhong,Yang, Bin,et al. Study on salt spray corrosion of Ni-graphite abradable coating with 80Ni20Al and 96NiCr-4Al as bonding layers[J]. SURFACE & COATINGS TECHNOLOGY,2011,205(17-18):4154-4161.
APA Xu, Cunguan,Du, Lingzhong,Yang, Bin,Zhang, Weigang,&Zhang, WG.(2011).Study on salt spray corrosion of Ni-graphite abradable coating with 80Ni20Al and 96NiCr-4Al as bonding layers.SURFACE & COATINGS TECHNOLOGY,205(17-18),4154-4161.
MLA Xu, Cunguan,et al."Study on salt spray corrosion of Ni-graphite abradable coating with 80Ni20Al and 96NiCr-4Al as bonding layers".SURFACE & COATINGS TECHNOLOGY 205.17-18(2011):4154-4161.
Files in This Item:
File Name/Size DocType Version Access License
20131105-912-复件 1-s2(2161KB)期刊论文出版稿限制开放CC BY-NC-SAApplication Full Text
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Xu, Cunguan]'s Articles
[Du, Lingzhong]'s Articles
[Yang, Bin]'s Articles
Baidu academic
Similar articles in Baidu academic
[Xu, Cunguan]'s Articles
[Du, Lingzhong]'s Articles
[Yang, Bin]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Xu, Cunguan]'s Articles
[Du, Lingzhong]'s Articles
[Yang, Bin]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.