Industry experiment & effect of oxidation resistance coating for steel slab
XIA Xiaoming; SUN Mingjun; WANG Wei; ZHAO Nan; WEI Lianqi
2012
Source PublicationBaosteel Technical Research
Issue04Pages:11-15
AbstractSpraying test were conducted twice before steel slabs were put into the furnace and the effects of the oxidation resistance coating were investigated and verified.By comparing the change of slab weight,rolling force of the roughing mill & finishing mill,thickness of oxide film on the surface slabs by an XL-30 SEM and acid pickling speed of slabs with and without coating,it was found that the oxidization waste in the furnace decreased by 40 percent with the use of the coating and the corresponding yield capacity could increase by 0.2 percent at least.Besides,the thickness of oxide scale film on hot rolled products was reduced by 1.44 micrometers and the acid pickling time was shortened by 6s with the coating technology,while the total rolling force of RM & FM did not changed.Furthermore,the application prospect of this technology was also discussed in this paper.
KeywordOxidation Resistance Coating Oxide Scale Oxidation Waste Rolling Force Pickling
Indexed BySCI
Document Type期刊论文
Version出版稿
Identifierhttp://ir.ipe.ac.cn/handle/122111/6977
Collection研究所(批量导入)
Recommended Citation
GB/T 7714
XIA Xiaoming,SUN Mingjun,WANG Wei,et al. Industry experiment & effect of oxidation resistance coating for steel slab[J]. Baosteel Technical Research,2012(04):11-15.
APA XIA Xiaoming,SUN Mingjun,WANG Wei,ZHAO Nan,&WEI Lianqi.(2012).Industry experiment & effect of oxidation resistance coating for steel slab.Baosteel Technical Research(04),11-15.
MLA XIA Xiaoming,et al."Industry experiment & effect of oxidation resistance coating for steel slab".Baosteel Technical Research .04(2012):11-15.
Files in This Item:
File Name/Size DocType Version Access License
Industryexperime_省略_(317KB)期刊论文出版稿限制开放CC BY-NC-SAApplication Full Text
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[XIA Xiaoming]'s Articles
[SUN Mingjun]'s Articles
[WANG Wei]'s Articles
Baidu academic
Similar articles in Baidu academic
[XIA Xiaoming]'s Articles
[SUN Mingjun]'s Articles
[WANG Wei]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[XIA Xiaoming]'s Articles
[SUN Mingjun]'s Articles
[WANG Wei]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.